(+86)0516- 68387188
Introduction: A lightweight medium-strength alloy formed by adding elements such as magnesium and silicon to an aluminum matrix, featuring good plasticity, corrosion resistance, and workability.
Application areas: Widely used in lightweight components such as aerospace, automotive, rail transit, and mechanical manufacturing structural parts
| Product Details | ||||
Product Name | Medium-strength aluminumA40X | |||
Main particle size range | 0-25μm | 15-53μm | 45-105μm | 75-150μm |
liquidity | 15-53μm | ≤100 s/50g | ||
bulk density | ≥1.2 g/cm3 | |||
tap density | ≥1.6 g/cm3 | |||
oxygen content | ≤300 ppm | |||
nitrogen content | ≤300 ppm | |||
mechanical properties | Temperature: Room temperature Tensile strength/Mpa ≥440 Yield strength/Mpa ≥300 Elongation after fracture, % ≥ 8 Section elongation rate/% ≥13 | |||
|